Acero rápido de herramientas m2 thixoconformado

  1. CABEZA SIMO MARTA M.
Supervised by:
  1. J. I. Verdeja González Director

Defence university: Universidad de Oviedo

Year of defence: 1997

Committee:
  1. José Antonio Pero-Sanz Elorz Chair
  2. José P. Sancho Martínez Secretary
  3. José Maria Rodriguez Ibabe Committee member
  4. Francisco Menéndez García Committee member
  5. Juan José del Campo Gorostidi Committee member

Type: Thesis

Teseo: 60093 DIALNET

Abstract

SE HAN COMPARADO MICROESTRUCTURALMENTE PIEZAS, EN ESTADO DE SERVICIO -BONIFICADAS- FABRICADAS POR THIXOCONFORMADO -CONFORMADO EN ESTADO SEMISOLIDO- DE ACEROS RAPIDOS PARA HERRAMIENTAS M2 OBTENIDOS BIEN POR FORJA -PROCESO GFM- O ATOMIZACION DE POLVOS PREALEADOS- PROCESOS OSPREY-, CON LAS DEL MISMO ACERO M2 FABRICADAS POR METODO CONVENCIONAL.LAS CONCLUSIONES MUESTRAN QUE LOS ACEROS THIXOCONFORMADOS PRESENTAN UNA MICROESTRUCTURA ESFEROIDADL, FINA Y UNIFORME QUE ASEGURA LA ISOTROPIA DE PROPIEDADES MECANICAS. AL CONTRARIO QUE LAS PIEZAS CONVENCIONALES QUE MUESTRAN RESISTENCIAS LONGITUDINALES MUY SUPERIORES A LAS TRANSVERSALES. LA ELIMINACION DE LA POROSIDAD RESIDUAL E INCLUSIONES PROVENIENTES DEL MOLDE EN ACEROS M2 THIXOCONFORMADOS, PERMITIRIAN IGUALAR SUS PROPIEDADES MECANICAS Y RESISTENCIA AL DESGASTE CON LAS DE ESTOS ACEROS EN ESTADO FORJADO. CON LA VENTAJA ADICIONAL DE QUE LAS PRESIONES DE FORJA RESULTARIAN MIL VECES MAS BAJAS.